UL type MoSi2 heating element for furnace

We make 1700C and 1800C UL shape MoSi2 heating elements, high quality, fast delivery, very competitive price

We are professional manufacturer of high quality MoSi2 heating elements.

Any sized elements can be made according to your requirement.

We can make U, W, UL, WL, and ROD type elements According to the highest working temperature we have 1700C and 1800C types.

The standard diameters are: 3/6mm, 4/9mm, 6/12mm, 9/18mm, 12/24mm.

MoSi2 heating elements physical and chemical characters:

1. Physical Characters

Volume Density	Bending Strength	Vickers Hardness	Porosity	Water absorption	Heating Elongation Rate
5.5 g/cm3	15-25 kg/cm3	(HV)570kg/mm2	7.4%	1.2%	4%

2. Chemical CharacterMoSi2 heating element is used in the high temperature under oxidizing atmosphere. It will form the SiO2 film which can keep the element from being melted. During the oxidizing process, the SiO2 protecting film is formed again when the element continues to be used. The MoSi2 heating element must not be used in the temperature between 400C and 700C for a long time, otherwise the element will be cremated under the strong oxidizing function in the low temperature.

MoSi2 heating element can usually make use of furnace temperature from 1300C to 1800C. It is extensively used in the industries of metallurgy, glass, ceramic refractory, crystal electronic device, industrial furnace manufacture, etc.. It is an essential ideal element when the products are sintering in the high temperature.